PP 宁波台塑 5090T
物性表
性能项目 | 测试条件 | 测试方法 | 数值/描述 | 单位 | |
机械性能 | 拉伸强度(引张强度) | ASTM D638/ISO527 | kg/cm²(MPa)[Lb/in2] | ||
断裂伸长率 | ASTM D638/ISO527 | % | |||
拉伸模量 | ASTM D638/ISO527 | kg/cm²(MPa)[Lb/in2] | |||
拉伸屈服伸长率(延伸率) | ASTM D638/ISO527 | % | |||
拉伸断裂伸长率(延伸率) | ASTM D638/ISO527 | 300 | % | ||
弯曲模量(弯曲弹性率) | ASTM D790/ISO178 | 932 | kg/cm²(MPa)[Lb/in2] | ||
弯曲强度 | ASTM D790/ISO178 | kg/cm²(MPa)[Lb/in2] | |||
洛氏硬度 | ASTMD785 | 98 | |||
IZOD 缺口冲击强度 | 1/4" 23℃ | ASTM D256/ISO179 | 8 | kg·cm/cm(J/M)ft·lb/in | |
1/4"-30℃ | ASTM D256/ISO179 | kg·cm/cm(J/M)ft·lb/in | |||
1/8" 23℃ | ASTM D256/ISO179 | kg·cm/cm(J/M)ft·lb/in | |||
1/8"-30℃ | ASTM D256/ISO179 | kg·cm/cm(J/M)ft·lb/in | |||
Charpy冲击强度 | 23℃ (缺口) | ASTM D256/ISO179 | kg·cm/cm(J/M)ft·lb/in | ||
-30℃(缺口) | ASTM D256/ISO179 | kg·cm/cm(J/M)ft·lb/in | |||
23℃(无缺口) | ASTM D256/ISO179 | kg·cm/cm(J/M)ft·lb/in | |||
-30℃(无缺口) | ASTM D256/ISO179 | kg·cm/cm(J/M)ft·lb/in | |||
物性性能 | 比重(密度) | ASTM D792/ISO1183 | 0.9 | ||
成型收缩率 | ASTMD955 | 1.3-1.7 | % | ||
熔融指数(流动系数) | 200℃/5kg | ASTMD1238/ISO 1133 | 14 | g/10min | |
220℃/10kg | ASTMD1238/ISO 1133 | g/10min | |||
吸水率 23℃/24H | ASTM D570/ISO62 | % | |||
热性能 | 热变形温度 | 退火 | ASTM D648/ISO75 | ℃(℉) | |
未退火 | ASTM D648/ISO75 | 95 | ℃(℉) | ||
维卡软化点 | ASTMD1525/ISO R306 | 125 | ℃(℉) | ||
熔点 | - | ℃(℉) | |||
燃烧性(率) | UL94 | ||||
线性膨胀系数 | ASTM D696/ISO11359 | mm/mm.℃ | |||
加工条件 | 干燥条件 | ||||
加工温度 | 射嘴 | ℃ | |||
料筒前段 | ℃ | ||||
料筒中段 | ℃ | ||||
料筒后段 | ℃ | ||||
熔体温度 | ℃ | ||||
模具温度 | ℃ | ||||
压力 | 注塑压力 | Mpa | |||
保压压力 | Mpa | ||||
背压 | Mpa | ||||
螺杆转速 | rpm | ||||
其他 | 备注 | 符合FDA 21 CFR 177.1520规定。高透明性、抗化学、药品质佳 | |||
颜色 | 高透明 | ||||
特性 | |||||