PC/ABS T65 XF 易流动

T65 XF牌号简介：（PC+ABS）混合物；未增强；注塑等级；VICAT/B120温度=120°C；与T65相比流动性得到改善。

厂家：德国科思创

类别：PC+ABS

加工条件：注射成型

性能特点：HB; 易流动;

Bayblend® FR3002 物性描述：(PC+ABS)-Blend; flame retardant; Vicat/B120 temperature = 99 °C; UL recognition 94 V-0 (1.0 mm); glow wiretemperature (GWFI): 960 °C at 2.0 mm; for notebooks and thinwallapplications

Bayblend® FR3008 物性描述：(PC+ABS)-Blend; flame retardant; Vicat/B120 temperature = 103 °C; improved chemical resistance; HDT/A >=85 °C; UL recognition 94 V-0 at 1.5 mm; glow wire temperature(GWFI): 960 °C at 2.0 mm; good light stability

Bayblend® FR3009物性描述：(PC+ABS)-Blend; flame retardant; Vicat/B120 temperature = 103 °C; UL recognition 94 5VB at 1.8 mm;successor to FR3000 BBS066; Improved hydrolysis resistance

Bayblend® FR3010 物性描述：(PC+ABS)-Blend; flame retardant; Vicat/B120 temperature = 110 °C; increased heat resistance; UL recognition94 V-0 at 1.5 mm; glow wire temperature (GWFI): 960 °C at 2.0 mm;improved chemical resistance and stress cracking behavior;successor to FR2010

Bayblend® FR3011 物性描述：(PC+ABS)-Blend; flame retardant; easyflowing; Vicat/B 120 temperature = 118 °C; good heat resistance; ULrecognition 94 V-0 at 1.5 mm; glow wire temperature (GWFI): 960 °Cat 2.0 mm; good light stability

Bayblend® FR3012 物性描述：(PC+ABS)-Blend; flame retardant; Vicat/B120 temperature = 102 °C; UL recognition 94 V-1 (1.5 mm); goodlight stability

Bayblend® FR3013 物性描述：(PC+ABS)-Blend; flame retardant; impactmodified; easy flowing; Vicat/B 120 temperature = 95°C; for:information technology

Bayblend® FR3020 物性描述： (PC+ABS)-Blend; 5 % mineral filled; flameretardant; Vicat/B 120 temperature = 103 °C; HDT/A >= 85 °C; forthin-wall applications; very good UL recognition in small wallthicknesses (V-0 at 0.75 mm); low smoke density

Bayblend® FR3021 物性描述： (PC+ABS)-Blend; 15 % mineral filled;flame retardant; Vicat/B 120 temperature = 98 °C; high stiffness;tensile modulus = 4800 MPa;; UL recognition 94 V-0 at 1.5 mm; glowwire temperature (GWFI): 960 °C at 2.0 mm

Bayblend® FR3025 物性描述：(PC+ABS)-Blend; flame retardant; mineralfilled ; Vicat/B 120 temperature = 102 °C; UL recognition 94 V-0 at1.2 mm; low warpage; improved stiffness and surface quality; fornotebooks and thinwall applications

Bayblend® FR3030 物性描述： (PC+ABS)-Blend; flame retardant; Vicat/B120 temperature = 115°C; extrusion grade; good extrusion andvacuum-forming behaviour; UL recognition 94 V-0 at 1.5 mm;halogen-free according to DIN VDE 0472,815; glow wire temperature(GWFI): 960 °C at 1.0 mm

干燥处理：加工前的干燥处理是必须的。湿度应小于0.04%，建议干燥条件为90~110C，2~4小时。

注射速度：尽可能地高。

化学和物理特性: PC/ABS具有PC和ABS两者的综合特性。

例如ABS的易加工特性和PC的优良机械特性和热稳定性。二者的比率将影响PC/ABS材料的热稳定性。PC/ABS这种混合材料还显示了优异的流动特性。收缩率在0.5%左右。